Reshock Response of 2A12 Aluminum Alloy at High Pressures

By means of mounting the specimen on a low-impedance buffer, reshock experiments were carried out on a 2A12 aluminum alloy up to shock stresses of 67.6 GPa. Reshock wave profiles from the initial shock stresses of 60.9–67.6 GPa were measured with a velocity interferometer, and it shows that the 2A12 aluminum alloy characterizes as quasi-elastic response during recompression process. The Lagrange longitudinal velocities along the reloading path from initial shock state were obtained from two shots of experiments, while the bulk velocities at corresponding shock stresses were determined via extrapolating from the public reported unloading plastic sound velocities. Combining the reshock and the release experimental results, the yield strength of 2A12 aluminum alloy at shock stress of 60.9 GPa was estimated to be about 1.7 GPa