The electrochemical corrosion of maraging steel in various media

Electrochemical corrosion behavior of maraging steel in various media has been studied using electrode kinetic measurements. The media used included IN H/sub 2/SO/sub 4/, IN HCl and artificial sea water, all at room temperature. The steel used was 350 grade of maraging steel and its corrosion behavior was studied in annealed as well as aged condition. In addition to the general behavior observed using potentiodynamic polarization, the corrosion rates were also evaluated using our own method known as ZTCorr. This method has been proved to be robust and accurate as compared to any other known method. The surfaces of corroded specimens were examined in an scanning electron microscope. The pitting observed in samples corroded by sea water was found to be associated with the inclusion present in the steel. Passive behavior was noted in IN H/sub 2/SO/sub 4/ but not IN HCl or artificial sea water. (author)