Phase composition and low frequency internal friction of ZrO2 + 4 mol.% Y2O3 ceramics
Creators
- 1. Donetskij Fiziko-Tekhnicheskij Inst. NAN Ukrainy, Donetsk (Ukraine)
Description
Under 24 Hz frequency of torsional oscillations one studied the low-frequency internal friction of ZrO2+4 mol.%YbO3 ceramics polycrystalline specimens resulting from the powder cold isostatic compaction followed by the air sintering, the hot isostatic argon compaction of the mentioned specimens followed by surface mechanical deformation and further air annealing. By means of X-ray phase analysis one investigated into the effect of the phase composition upon specimen surface mechanical deformation and its subsequent air annealing. The internal friction was measured within 280-380 K temperature range using a specimen upon its air annealing. Under 315 K temperature one revealed the internal friction peak resulting from stress relaxation at T'-phase domain boundaries
Abstract (Russian)
При частоте крутильных колебаний 24 Гц исследовано низкочастотное внутреннее трение поликристаллических образцов керамики ZrO2 + 4 мол.% Y2O3, изготовленных с использованием холодного изостатического прессования порошка с последующим спеканием на воздухе, горячим изостатическим прессованием этого образца в атмосфере аргона, с последующей механической деформацией поверхности и дальнейшим обжигом на воздухе. Методом рентгенофазного анализа исследовано изменение фазового состава после механической деформации поверхности образца и последующего его обжига на воздухе. Внутреннее трение измерялось в интервале температур 280-380 К на образце после его обжига на воздухе. При температуре 315 К обнаружен пик внутреннего трения, который объясняется релаксацией напряжений на границах доменов T'-фазыAdditional details
Additional titles
- Original title (Russian)
- Фазовый состав и низкочастотное внутреннее трение керамики ZrO
Publishing Information
- Journal Title
- Fizika Tverdogo Tela
- Journal Volume
- 48
- Journal Issue
- 9
- Journal Page Range
- p. 1590-1592
- ISSN
- 0367-3294
- CODEN
- FTVTAC
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 39078715
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CERAMICS; CRYSTAL-PHASE TRANSFORMATIONS; CUBIC LATTICES; DEFORMATION; HEAT TREATMENTS; INTERNAL FRICTION; PHASE STUDIES; POLYCRYSTALS; SINTERED MATERIALS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0273-0400 K; TEMPERATURE RANGE 1000-4000 K; TETRAGONAL LATTICES; TRANSITION TEMPERATURE; YTTRIUM OXIDES; ZIRCONIUM OXIDES
- Descriptors DEC
- CHALCOGENIDES; CRYSTAL LATTICES; CRYSTAL STRUCTURE; CRYSTALS; FRICTION; MATERIALS; OXIDES; OXYGEN COMPOUNDS; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS; YTTRIUM COMPOUNDS; ZIRCONIUM COMPOUNDS
Optional Information
- Notes
- 8 refs., 2 figs., 1 tab.