Effect of composition on the degree of anisotropy of thermal expansion and electric resistance of cermet specimens of GeTe

A study was made on α temperature coefficient of thermal expansion and ρ specific electric resistance of cermet germanium telluride for alloys close to stoichiometric composition. It is shown that anisotropy of thermal expansion of cermet germanium telluride depends sufficiently on its composition. This dependence is clearly pronounced if tellurium content in alloys equals 50.4-51.2 at.%. The maximal anisotropy is observed in the alloy containing 50.8 at.% of tellurium. The temperature of extreme value of temperature coefficient of linear expansion decreases from 440 down to 373 deg.C for alloys with 49-50.8 at.% of tellurium, and grows from 373 up to 405 deg.C if tellurium content equals 50.8-52 at.%