Identification of acoustic emission sources in early stages of fatigue process of Inconel 713LC

Inconel 713LC is low carbon variant of Inconel 713 nickel-based cast alloy. The biggest advantage of these alloys is their ability to resist a wide variety of operating conditions (corrosive environment, high temperature, high stresses). Main area of applications is aircraft, energetic, chemical and petrochemical industry etc. In many applications, components undergo cyclic stresses. This study presents results of acoustic emission response of Inconel 713LC during high-cycle fatigue testing. In comparison with low-cycle fatigue, stage of initiation of micro cracks is in high-cycle region much more significant and can take several tens of percent of whole fatigue life. This work is focused on comparison of selected parameters of acoustic emission signal in pre-initiation and initiation stage of fatigue crack creation. Signal data were specified by linear location technique, hence only signal from shallow notch was analysed. Acoustic emission signal was correlated with frequency of load reversals which is a function of specimen's rigidity (modulus). Acoustic emission hits with higher stress were detected in pre-initiation stage whereas initiation stage hits exhibited low stress. Acoustic emission signal measurements are supplemented by fractographic and metallographic analysis.