Low temperature dependence of elastic moduli and internal friction for the glassy alloy Zr55Cu30Al10Ni5

Longitudinal and transverse wave velocities, eight kinds of elastic parameters, and dilational and shear internal frictions of Zr55Cu30Al10Ni5 glassy alloy were simultaneously measured as a function of temperature in the range from 77 to 373 K, using an ultrasonic pulse method. The inflections at around 150 K for wave velocities, anisotropy factor and Poisson's ratio, and the 150 K peak of shear friction seem to correspond to one topological change (pseudo-transition) associated with an interatomic readjustment or vacancy rearrangements. The behaviors from 77 to 125 K and 125 to 373 K are due to thermal relaxation of squeezed free volumes and entropy elasticity associated with vibrational motions of clusters, respectively, accompanied by an increase in atomic distance. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)