Effect of gamma irradiation on biopolymer composite films of poly(vinyl alcohol) and bacterial cellulose

Highlights: ► The paper reports the obtaining of composite materials between PVA and BC. ► The composite films were γ-irradiated at doses up to 50 kGy. ► The films have a good resistance, being suitable as food packaging materials. - Abstract: Composite materials containing in different ratios poly(vinyl alcohol) (PVA), bacterial cellulose (BC) and glycerol (G) as plasticizer were obtained and exposed to different γ radiation doses using an irradiator GAMMATOR provided with 137Cs source. These films successively received up to 50 kGy absorbed doses at a dose rate of 0.4 kGy/h at room temperature. In order to study the chemical and structural changes during γ irradiation, Fourier-transformed infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and UV–Vis spectroscopy were used. Water vapour permeability (WVP), Hunter colour parameters and hardness were also measured for the irradiated samples. Investigation revealed that WVP was not significantly affected by the irradiation. Colour measurements indicated a slight decrease of pure PVA films transparency and it made clear that all samples became more reddish and yellowish after irradiation. The samples hardness was not affected by the irradiation doses used. However, the results showed no drastic structural or chemical changes of the irradiated samples, which prove, in consequence, a good durability. These composite materials could be used as packaging materials for γ irradiated products.