Integration of porosity and bio-functionalization to form a 3D scaffold: cell culture studies and in vitro degradation

In this study, porous poly(lactide-co-glycolide) (PLGA) (50/50) microspheres have been fabricated by the gas-foaming technique using ammonium bicarbonate as a gas-foaming agent. Microspheres of different porosities have been formulated by varying the concentration of the gas-foaming agent (0%, 5%, 10% and 15% w/v). These microspheres were characterized for particle size, porosity and average pore size, morphology, water uptake ratio and surface area and it was found that the porosity, pore size and surface area increased on increasing the concentration of the gas-foaming agent. Further, the effect of porosity on degradation behavior was evaluated over a 12 week period by measuring changes in mass, pH, molecular weight and morphology. Porosity was found to have an inverse relationship with degradation rate. To render the surface of the microspheres biomimetic, peptide P-15 was coupled to the surface of these microspheres. In vitro cell viability, proliferation and morphological evaluation were carried out on these microsphere scaffolds using MG-63 cell line to study the effect of the porosity and pore size of scaffolds and to evaluate the effect of P-15 on cell growth on porous scaffolds. MTT assay, actin, alizarin staining and SEM revealed the potential of biomimetic porous PLGA (50/50) microspheres as scaffolds for tissue engineering. As shown in graphical representation, an attempt has been made to correlate the cell behavior on the scaffolds (growth, proliferation and cell death) with the concurrent degradation of the porous microsphere scaffold as a function of time.