TEM observations of HT-9 as-welded weldment microstructures

TEM studies of different locations in an HT-9 weldment indicated delta-ferrite (delta) occurrence, M23C6 precipitation at delta-martensite interfaces, fine carbide precipitation at prior austenite grain boundaries, and martensite lath and lath packet size to be the distinguishable microstructure features observed. Furthermore, retained austenite films were observed in the weld metal and the HAZ adjacent to the weld metal that reached the highest temperature during joining. The microstructures correlate well with the observed room temperature microhardness except for the fusion boundary in weld metal which exhibited a hardness drop and an unexpected minimum amount of delta-ferrite