Mn doping effect on optical and ESR studies of Zn_1-xMn_xO compound sintered at different temperatures

Polycrystalline bulk samples of Zn_1-xMn_xO with x=0.02, 0.04, 0.05 and sintered at different temperatures (500 °C & 800 °C) were studied to investigate the doping effect on the structural, optical properties and spin dynamics in ZnO system. The crystallite size was seen to decrease with no significant change in other structural parameters. FTIR study showed a small effect on the Zn-O stretching bond and other bonds due to presence of Mn. Calculation from UV-Vis spectra showed increase in the optical band gap in the low temperature sintered samples due to Mn doping. In the PL spectra, the UV emission seen to dominate for the 500 °C sintered sample, for 800 °C sample the visible emission dominate indicating increase in non-radiative emission. ESR signals obtained from the microwave absorption shows ferromagnetic signal for the low temperature sintered sample only with a g value of 2.004 for the 2% Mn doped sample. The number of spin participation for resonance is calculated from the ESR signal, which supports the magnetic behaviour of this particular sample.