Hysteresis effect in crack propagation in the threshold range of very strong steel 21 CrMoNiV 57
Creators
- 1. GKSS-Forschungszentrum Geesthacht GmbH, Geesthacht-Tesperhude (Germany, F.R.). Inst. fuer Werkstofforschung
Description
The very strong steel 21 CrMoNiV 57 showed the following crack propagation behaviour in the threshold range: - The threshold value decreased with increasing R value as expected. - Regardless of the R ratio and the threshold value reached, the hysteresis effect was found during subsequent increase in load, even if there was no crack closing (R = 0.7 = Reff). - The DELTAK range in which the crack could not spread, lay 25% to 38% above the threshold value reached. - According to metallurgical investigations, the cause of the hysteresis effect lay in the fact that the crack stops at micro-structural obstacles. This also leads to relaxation of the DELTAK and DELTAKeff concept. (orig.)
Availability note (English)
Available from Deutscher Verband fuer Materialforschung und -pruefung e.V., Berlin (Germany, F.R.).Abstract (German)
Der hochfeste Stahl 21 CrMoNiV 57 zeigte folgendes Rissausbreitungsverhalten im Schwellwertbereich: Der Schwellwert nahm mit zunehmendem R-Wert erwartungsgemaess ab. Unabhaengig vom R-Verhaeltnis und vom erreichten Schwellwert wurde waehrend der anschliessenden Lasterhoehung der Hysterese-Effekt festgestellt, auch dann, wenn es keine Rissschliessung gab (R = 0,7 = Reff). Der ΔK-Bereich, in dem sich der Riss als nicht ausbreitungsfaehig erwies, lag 25% bis 38% oberhalb des erreichten Schwellwertes. Nach metallographischen Untersuchungen liegt die Ursache des Hysterese-Effekts darin, dass der Riss an mikrostrukturellen Hindernissen zum Stehen kommt. Dies fuehrt zugleich zur Aufweichung (relaxation) des ΔK- und des ΔKeff-Konzeptes. (orig.)Additional details
Additional titles
- Original title (German)
- Hysterese-Effekt bei der Rissausbreitung im Schwellwertbereich des hochfesten Stahls 21 CrMoNiV 57
Publishing Information
- Imprint Title
- 20 years DVM Study Group 'Fracture Mechanisms'
- Imprint Pagination
- 550 p.
- Journal Page Range
- p. 225-235.
Conference
- Title
- Fracture-mechanical characteristics for structural components evaluation.
- Original Conference Title
- 21. Vortragsveranstaltung des DVM-Arbeitskreises Bruchvorgaenge: Bruchmechanische Kennwerte fuer die Bauteilbewertung
- Acronym
- 21. lecture meeting of the DVM Study Group 'Fracture Mechanisms'
- Dates
- 27-28 Feb 1989.
- Place
- Bad Nauheim (Germany, F.R.).
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 22002594
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference, Non-conventional Literature
- Descriptors DEI
- CRACK PROPAGATION; FATIGUE; FRACTURE MECHANICS; HYSTERESIS; METALLOGRAPHY; MICROSTRUCTURE; STEEL-CRMOV
- Descriptors DEC
- ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; COPPER ADDITIONS; CRYSTAL STRUCTURE; IRON ALLOYS; IRON BASE ALLOYS; LOW ALLOY STEELS; MECHANICAL PROPERTIES; MECHANICS; MOLYBDENUM ADDITIONS; NICKEL ADDITIONS; STEELS; VANADIUM ADDITIONS
Optional Information
- Notes
- Imprint:20 Jahre DVM-Arbeitskreis Bruchvorgaenge.;Bruchmechanische Kennwerte fuer die Bauteilbewertung.