Influence of crosslinker structure on performance of functionalised organic-inorganic hybrid sol-gel coating

This research aimed to investigate the influence of the co-condensation of the three different organofunctional trialkoxysilane precursors with two different crosslinkers, i.e. tetraethoxysilane or organocyclotetrasiloxane on the performance and the washing fastness of this multicomponent multifunctional sol-gel coating on cellulose fibres. To this aim, a three-component equimolar sol mixture (MC), which included 1H,1H,2H,2H-perfluorooctyltriethoxysilane (SiF), 3-(trimethoxysilyl)-propyldimethyloctadecyl ammonium chloride (SiQ) and P,P-diphenyl-N-(3-(trimethoxysilyl)propyl) phosphinic amide (SiP) in combination with two different concentrations of TEOS (T and 3T) or organocyclotetrasiloxane 2,4,6,8-tetrakis(2-(diethoxy(methyl)silyl)ethyl)-2,4,6,8-tetramethyl–cyclotetrasiloxane (T₄) as crosslinkers, was applied to the cotton fibres by a pad-dry-cure process. The functional properties of the coated samples before and after repeated washing were investigated by the water θ (W) and n-hexadecane θ (C16) static contact angle as well as water sliding (roll-off) (α) angle measurements. The inclusion of both TEOS and T₄ into the MC sol increased the hydrophobic affect and simultaneously decreased the oleophobic effect of the MC coating. These phenomena were more pronounced for higher concentration of TEOS and T₄ crosslinker. The inclusion of T₄ into the MC sol improved the coating washing fastness to a significantly higher extent than the inclusion of TEOS, with respect to the applied concentrations. (paper)