Effect of annealing temperature on the mechanical properties of zircaloy-4 cladding

The mechanical properties of zircaloy cladding materials are sensitive to those fabrication variables which have an effect on the preferred crystallographic orientation or texture of the finished tube. The effect of one such variable, the final annealing temperature, on various mechanical properties is examined using tube reduced zircaloy-4 fuel rod cladding annealed at temperatures from 905F to 1060F. This temperature range provides cladding with varying degrees of recrystallization including full recrystallization. Hoop creep characteristics of zircaloy cladding were studied as a function of the annealing temperature using closed-end internal pressurization tests at 750F and hoop stresses of 10, 15, 20 and 25 ksi. The critical annealing temperature at which a minimum creep strain occurs decreases as the applied stress increases. An additional test at 700F and 30 ksi hoop stress was conducted to demonstrate that the critical annealing temperature is essentially independent of the test temperature. Plausible explanations based on differing substructures developed in cold-worked stress-relieved material are forwarded. The effect of annealing temperature on the room temperature mechanical anisotropy parameters, R and P, was studied. R-parameters were determined from in situ transverse strain gage measurements in uniaxial tensile tests. P-parameters were calculated from uniaxial test data (R and yield stress) and hoop yield stress determined in biaxial, closed-end internal pressurization tests