Effect of repressing of briquettes at high hydrostatic pressures on fine structure of carbide fraction in compacts and sintered BK10 alloy

The effect was studied of the repressing at high hydrostatic pressures of preforms of hard alloy powder mixture with different degree of fineness on changes in fine structure of the carbide phase of compacts and the VK10 sintered alloy. X-ray diffraction method was used. Sufficient widening of diffraction lines of the WC phase in compacts and in a sintered alloy with the increase in hydrostatic pressure testifies to the fact of the production of more inperfect carbide substructure mainly due to fragmentation subgrains. The effect of processing pressure manifests itself to a greater extent in compacts of the coarse-ground mixture; in the sintered alloy the repressing pressure effect ''is being smoothed'' to some extent. The density of dislocation in the compacts and the sintered alloy were evaluated quantatively depending on the hydrostatic pressure values during processing of preforms