Determination of crack arrest toughness at high temperatures using compact specimens

Creators

  • 1. Stuttgart Univ. (Germany, F.R.). Staatliche Materialpruefungsanstalt

Description

In order to determine the influence of the test temperature on the crack arrest toughness, investigations were carried out on pressure vessel steels of various strength and toughness up to the upper-shelf of the Charpy V-notch impact energy (CV-energy). The tests were conducted on the basis of the proposed ASTM test method for ferritic steels (20 MnMoNi 55, 22 NiMoCr 37, 17 MoV 84) with modified wedge-loaded compact specimens. The thickness ranged from 19 to 170 mm, the in-plane dimensions from 100 to 400 mm. The comparison with the reference curves of the American and German guidelines showed significant discrepancies at higher temperatures. (orig./HP)

Abstract (German)

Zur Ermittlung des Einflusses der Prueftemperatur auf die Rissstopp-Zaehigkeit wurden an Druckbehaelterstaehlen unterschiedlicher Festigkeit und Zaehigkeit Untersuchungen bis in den Bereich der Hochlage der Kerbschlagarbeit durchgefuehrt. Es wurde auf der Grundlage des ASTM-Normentwurfs fuer ferritische Werkstoffe (20 MnMoNi 55, 22 NiMoCr 37, 17 MoV 84) an modifizierten, transversal keilbelasteten Compact-Proben mit Dicken bis zu 170 mm und Probenhoehen bis 400 mm geprueft. Ein Vergleich der Ergebnisse mit den Referenzkurven der amerikanischen und deutschen Regelwerke (ASME III, ASME XI und KTA) zeigte bei hohen Temperaturen deutliche Abweichungen. (orig./HP)

Additional details

Additional titles

Original title (German)
Rissstopp-Untersuchungen bei hohen Temperaturen an keilbelasteten Compact-Proben

Publishing Information

Journal Title
Materialpruefung
Journal Volume
29
Journal Issue
11/12
Series
Materialpruefung.
Journal Page Range
340-345
ISSN
0025-5300
CODEN
MTPRA

INIS

Country of Publication
Germany
Country of Input or Organization
Germany
INIS RN
19039847
Subject category
S36: MATERIALS SCIENCE; S22: GENERAL STUDIES OF NUCLEAR REACTORS;
Descriptors DEI
CHARPY TEST; CHROMIUM-NICKEL STEELS; CRACK PROPAGATION; FERRITIC STEELS; FRACTURE PROPERTIES; LOW ALLOY STEELS; MOLYBDENUM ALLOYS; NOTCHES; PRESSURE VESSELS; TEMPERATURE DEPENDENCE; VANADIUM ADDITIONS
Descriptors DEC
ALLOYS; CARBON ADDITIONS; CHROMIUM ALLOYS; CONTAINERS; DESTRUCTIVE TESTING; HIGH ALLOY STEELS; IMPACT TESTS; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS TESTING; MECHANICAL PROPERTIES; MECHANICAL TESTS; NICKEL ALLOYS; STAINLESS STEELS; STEELS; TESTING

Optional Information

Contract/Grant/Project number
Contract BMFT 150 0304 B