Published August 2003 | Version v1
Journal article Metadata-only

Structure and mechanical properties of Al-Ni-Fe-La alloys after rapid hardening and annealing. Part I. Structure

Creators

  • 1. RAN, Inst. Metallurgii i Materialovedeniya im. A.A. Bajkova, Moscow (Russian Federation)

Description

On the basis of concepts of the influence of average electron concentrations in alloys on their tendency to render amorphous new alloys with an average electron concentrations ranging from 3.68 to 3.75 are designed and proposed. The structure is studied in Al base alloys (85 at. %) doped with Ni, Fe, La in various proportions, cooled with the rate of 106 deg C/c and then isothermically annealed at temperatures up to 400 deg C. It is revealed that an alloy of Al85Ni7Fe4La4 with an average electron concentration of e/a = 3.69 is most stable to thermal effect on continuous heating

Abstract (Russian)

На основе представлений о влиянии средней электронной концентрации в сплавах на их склонность к аморфизации разработаны и предложены новые сплавы со средней электронной концентрацией от 3.68 до 3.75. Изучена структура сплавов на основе Al (85 ат. %), легированных Ni, Fe, La в различных соотношениях, полученная после охлаждения со скоростью 106 град С/с и последующего изотермического отжига при температурах до 400 град С. Установлено, что устойчивостью к термическому воздействию при непрерывном нагреве обладает сплав Al85Ni7Fe4La4, средняя электронная концентрация которого e/a = 3.69

Additional details

Additional titles

Original title (Russian)
Структура и механические свойства сплавов системы Ал-Ни-Фе-Ла после быстрой закалки и отжига. Част' И. Структура

Publishing Information

Journal Title
Metallovedenie i Termicheskaya Obrabotka Metallov
Journal Issue
no.8
Journal Page Range
p. 16-21
ISSN
0026-0819
CODEN
MTOMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
36037740
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
ALUMINIUM BASE ALLOYS; AMORPHOUS STATE; ANNEALING; CRYSTALLIZATION; ELECTRONIC STRUCTURE; IRON ALLOYS; LANTHANUM ALLOYS; METALLIC GLASSES; MICROSTRUCTURE; NICKEL ALLOYS; PHASE STUDIES; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0400-1000 K
Descriptors DEC
ALLOYS; ALUMINIUM ALLOYS; HEAT TREATMENTS; PHASE TRANSFORMATIONS; RARE EARTH ALLOYS; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
6 refs., 4 figs., 5 tabs.