Electron beam processing of rubber wood fibers - polypropylene composites. Effects of reactive additives on the physical and mechanical properties

The purpose of this study is to determine the suitability of producing agro-fiber reinforced plastic composite (agro-FRPC) from rubber wood fiber blended in polypropylene matrix. The effects of varying fiber dimension and fiber content on the physical and mechanical properties of the composite were evaluated to provide an insight into the fiber matrix adhesion. The effects of reactive additives on the physical and mechanical properties of the composite were evaluated which provides the insight on the reinforcement of the composite. Rubber wood fiber used in this study is currently being used in the manufacturing of medium density fiber (MDF) board. Two sizes of rubber wood fiber were used i.e. 0.5-1.0 mm and 1.0-2.0 mm. Homopolymer polypropylene of MFI 14.0 was used as a matrix. The irradiation work was carried out using electron beam accelerator, 3.0 MeV, 3.0 mA. Various types of reactive additives (RA) with mono-functional, di-functional, tri-functional and oligomer were applied in the blend. For comparison, a conventional chemical cross-linking using two types of maleated polypropylene, MPA (Mw=9,000) and PMAP (Mw=220,000) were also performed. (author)