Facile synthesis, growth mechanism and reversible superhydrophobic and superhydrophilic properties of non-flaking CuO nanowires grown from porous copper substrates

Reversible superhydrophobic and superhydrophilic surfaces based on porous substrates covered with CuO nanowires are developed in this study. A facile thermal oxidation method is used to synthesize non-flaking bicrystalline CuO nanowires on porous copper substrates in static air. The effects of thermal oxidation temperature and duration are systemically studied. The growth mechanism of the obtained non-flaking CuO nanowires is presented and the compression stress is believed to be the key driving force. The wettability of the CuO nanowires after chemical modification with trichloro(1H,1H,2H,2H-perfluorooctyl)silane is systemically investigated. The porous substrates covered with CuO nanowires exhibit excellent superhydrophobic performance with almost no water adhesion and no apparent drag resistance, and a maximum static water contact angle of 162 ± 2° is observed. Moreover, a rapid reversibly switchable wettability between superhydrophobic and superhydrophilic states is realized by the alternation of air–plasma treatment and surface fluorination. The porous substrates covered with CuO nanowires will find promising applications in surface and corrosion protection, liquid transportation, oil–water separation, and self-cleaning surfaces. (paper)