Development of high-performance block fuel elements for high temperature reactors. Interim report
Creators
Description
Automatic translation: The pressed block element is to be used in the years 1972 - 1978 brought to technical maturity and tested in reactor tests. - Development of the graphite matrix In basic raw material investigations, phenolic resin binders thermogravimetrically tested for their coking behavior; Additions of hexamethylenetetramine as a hardener resulted in increased coke yields. To characterize graphite powders with different degrees of graphitization and therefore different processability, in addition to the complex X-ray measurement method the determination of baled density proved useful while Measurements of xylene density, bromine absorption, magnetic Susceptibility, the BET surface and the electrical conductivity are not very suitable for this. In the general graphite matrix program, the dependency of various matrix properties on the mixing ratio of the standard raw materials and on Manufacturing parameters examined. Both die-pressed at 150°C Samples as well as quasi-isostatically pressed balls were related Density, crack susceptibility, elongation-shrinkage behavior, anisotropy and strength compared.
Abstract (German)
Das gepreßte Blockelement soll in den Jahren 1972 - 1978 zur technischen Reife gebracht und in Reaktor tests erprobt werden. - Entwicklung der Graphitmatrix In Grundlagen-Rohstoffuntersuchungen wurden Phenolharz-Bindemittel thermogravimetrisch auf ihr Verkokungsverhalten geprüft; Zusätze von Hexamethylentetramin als Härter ergaben erhöhte Koksausbeuten. Zur Charakterisierung von Graphitpulvern mit unterschiedlichem Graphitierungsgrad und daher unterschiedlicher Verarbeitbarkeit hat sich neben der aufwendigen Röntgenmeßmethode die Bestimmung der Preßdichte als brauchbar erwiesen, während Messungen der Xyloldichte, der Bromabsorption, der magnetischen Suszeptibilität, der BET-Oberfläche und der elektrischen Leitfähigkeit hierfür wenig geeignet sind. Im allgemeinen Graphitmatrixprogramm wurde die Abhängigkeit verschiedener Matrixeigenschaften vom Mischungsverhältnis der Standard-Rohstoffe und von Herstellparametern untersucht. Sowohl bei 150°C gesenkgepreßte Proben als auch quasi-isostatisch gepreßte Kugeln wurden bezüglic Dichte, Rißanfälligkeit, Dehnungs-Schrumpfungsverhalten, Anisotropie und Festigkeit verglichen.
Files
Restricted
The record is publicly accessible, but files are restricted to users with access.
Additional details
Additional titles
- Original title (German)
- Entwicklung von Hochleistungsblockbrennelementen für Hochtemperaturreaktoren. Zwischenbericht
Publishing Information
- Imprint Pagination
- 93 p.
- Report number
- NUKEM--180
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- International Atomic Energy Agency (IAEA)
- INIS RN
- 53080070
- Subject category
- S21: SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS; S36: MATERIALS SCIENCE;
- Descriptors DEI
- BROMINE; COMPARATIVE EVALUATIONS; DENSITY; FEDERAL REPUBLIC OF GERMANY; FORSCHUNGSZENTRUM JUELICH; FUEL ELEMENTS; GRAPHITE; HTGR TYPE REACTORS; PERFORMANCE; PHENOLS; RAW MATERIALS; TEMPERATURE RANGE 0400-1000 K; X RADIATION; XYLENES
- Descriptors DEC
- ALKYLATED AROMATICS; AROMATICS; CARBON; DEVELOPED COUNTRIES; ELECTROMAGNETIC RADIATION; ELEMENTS; EUROPE; EVALUATION; GAS COOLED REACTORS; GERMAN FR ORGANIZATIONS; GRAPHITE MODERATED REACTORS; HALOGENS; HYDROCARBONS; HYDROXY COMPOUNDS; IONIZING RADIATIONS; MATERIALS; MINERALS; NATIONAL ORGANIZATIONS; NONMETALS; ORGANIC COMPOUNDS; PHYSICAL PROPERTIES; RADIATIONS; REACTOR COMPONENTS; REACTORS; TEMPERATURE RANGE; WESTERN EUROPE
Optional Information
- Notes
- 32 figs., 13 tabs.