Martensitic transformations and magnetic-field-induced strains in Ni50Mn50-xGax alloys
Creators
- 1. UrO RAN, Inst. Fiziki Metallov, Ekaterinburg (Russian Federation)
Description
A study is made into the concentration dependences of temperatures of direct and reverse martensitic transformations in alloys of Ni50Mn50-xGa x (x = 19-25) and into specific features of magnetic-field-induced jump-type elongation in a Ni50Mn28,5Ga21,5 alloy single crystal. A martensite monovariant state in the single crystal occurs due to compression under the action of both supporting magnetic field and mechanical load. It is shown that when using uniaxial mechanical compression at the curves of normal-magnetic-field-induced elongation several great jumps are observed which nature is associated with the formation of structural defects preventing displacement of martensite twins boundaries
Abstract (Russian)
Изучены концентрационные зависимости температуры прямого и обратного мартенситного превращения в сплавах Ni50Mn50-xGax (x = 19-25) и особенности индуцированного магнитным полем скачкообразного удлинения в монокристалле сплава Ni50Mn28,5Ga21,5. Моновариантное состояние мартенсита в монокристалле формировалось сжатием под воздействием как опорного магнитного поля, так и механической нагрузки. Показано, что при использовании одноосного механического сжатия на кривых удлинения, индуцированного приложением магнитного поля перпендикулярного направления, появляется несколько больших скачков, природа которых связывается с возникновением структурных дефектов, препятствующих смещению границ двойников мартенситаAdditional details
Additional titles
- Original title (Russian)
- Мартенситные превращения и магнитоиндуцированные деформации в сплавах Ни
Publishing Information
- Journal Title
- Fizika Metallov i Metallovedenie
- Journal Volume
- 102
- Journal Issue
- 2
- Journal Page Range
- p. 152-161
- ISSN
- 0015-3230
- CODEN
- FMMEA9
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 38029642
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ANISOTROPY; CHEMICAL COMPOSITION; COMPRESSION; CRYSTAL LATTICES; CRYSTAL-PHASE TRANSFORMATIONS; ELONGATION; GALLIUM ALLOYS; LATTICE PARAMETERS; MAGNETIC FIELDS; MAGNETIC SUSCEPTIBILITY; MANGANESE ALLOYS; MONOCRYSTALS; NICKEL BASE ALLOYS; PHASE STUDIES; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0065-0273 K; TEMPERATURE RANGE 0273-0400 K; TERNARY ALLOY SYSTEMS
- Descriptors DEC
- ALLOY SYSTEMS; ALLOYS; CRYSTAL STRUCTURE; CRYSTALS; DEFORMATION; MAGNETIC PROPERTIES; NICKEL ALLOYS; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 27 refs., 7 figs., 2 tabs.