Effect of the wave shocking treatment on the structure and strengthening of austenitic steels

Creators

  • 1. RAN, Inst. Metallurgii i Materialovedeniya im. A.A. Bajkova, Moscow (Russian Federation)

Description

The structure and hardening of austenitic manganese steels after shock wave treatment are studied. It is shown that the treatment results in the structure where an elementary cell size decreases with a pressure increase. The strain hardening resulted from shock wave loading can be estimated using a Hall-Petch equation. It is established that at similar degree of residual strains the shock wave loading compared to cold rolling gives rise to higher strengthening which value grows as austenite stacking fault energy decreases

Abstract (Russian)

Изучены структура и упрочнение аустенитных сталей после ударно-волновой обработки. Показано, что такая обработка формирует структуру, размер ячейки в которой уменьшается с повышением давления. Упрочнение сталей в результате ударно-волнового нагружения может быть оценено по уравнению Холла-Петча. Установлено, что при равных степенях остаточной деформации ударно-волновая обработка по сравнению с холодной прокаткой приводит к большему упрочнению, величина которого возрастает при снижении энергии дефектов упаковки аустенита

Additional details

Additional titles

Original title (Russian)
Влияние ударно-волновой обработки на структуру и упрочнение аустенитных сталей

Publishing Information

Journal Title
Metally (Moscow)
Journal Issue
no.2
Journal Page Range
p. 77-88
ISSN
0869-5733
CODEN
MEALET

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
37070171
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
AUSTENITIC STEELS; CHEMICAL COMPOSITION; DYNAMIC LOADS; HARDNESS; IMPACT SHOCK; MANGANESE STEELS; MICROSTRUCTURE; PRESSURE DEPENDENCE; PRESSURE RANGE MEGA PA 10-100; PRESSURE RANGE MEGA PA 100-1000; SHOCK WAVES; STACKING FAULTS; STRAIN AGING; STRAIN HARDENING; TENSILE PROPERTIES
Descriptors DEC
AGING; ALLOYS; CARBON ADDITIONS; CRYSTAL DEFECTS; CRYSTAL STRUCTURE; HARDENING; IRON ALLOYS; IRON BASE ALLOYS; MANGANESE ALLOYS; MECHANICAL PROPERTIES; PRESSURE RANGE; PRESSURE RANGE MEGA PA; STEELS; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
14 ref., 11 figs., 5 tabs.