Investigations by the Kossel-technique on grain boundary migration in strained tungsten in the presence of nickel
- 1. Max-Planck-Institut fuer Metallforschung, Stuttgart (Germany, F.R.). Inst. fuer Werkstoffwissenschaften
- 2. Technische Univ., Dresden (German Democratic Republic). Sektion Grundlagen des Maschinenwesens
Description
New grains formed in contact regions of cold compacted W and W (Ni) solid solution single crystal spheres during heating up to 1300 or 14700C when Ni was present. The newly formed grains grew during further annealing. The Kossel technique showed a reduction of the dislocation density of more than 5x109/cm2 in the wake of the migrating grain boundaries of the growing grains. The stress differences due to the dislocation density differences are in the correct order of magnitude to explain the observed boundary migration rates. an influence of diffusion induced grain boundary migration is not evident from these experiments. (orig.)
Abstract (German)
In den Kontaktbereichen kaltverpresster Proben aus einkristallinen W- und W-Mischkristallkugeln bildeten sich nach dem Aufheizen auf 1300 bis 14700C in Anwesenheit von Ni neue Koerner, die waehrend des weiteren Gluehens auf Kosten der Einkristalle wuchsen. Mit der Kossel-Technik wurde gezeigt, dass ein Versetzungsabbau um mehr als 5x109 Versetzungen/cm2 durch die wandernden Korngrenzen der wachsenden neuen Koerper erfolgte. Waehrend eine diffusionsinduzierte Korngrenzenwanderung aus den Versuchen nicht abgeleitet werden kann, liegen die durch den Versetzungsdichteunterschied aufgebauten Spannungen in der richtigen Groessenordnung, um die Wanderungsgeschwindigkeit der Korngrenzen zu erklaeren. (orig.)Additional details
Additional titles
- Original title (German)
- Kosseluntersuchungen zur Korngrenzenwanderung in verformtem Wolfram in Anwesenheit von Nickel
Publishing Information
- Journal Title
- Z. Metallkd.
- Journal Volume
- 77
- Journal Issue
- 6
- Series
- Z. Metallkd.
- Journal Page Range
- 368-376
- ISSN
- 0044-3093
- CODEN
- ZEMTA
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 18001440
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ANNEALING; COATINGS; DISLOCATIONS; GRAIN BOUNDARIES; GRAIN GROWTH; INTERFACES; KOSSEL METHOD; MONOCRYSTALS; NICKEL; POWDERS; SINTERED MATERIALS; SOLID SOLUTIONS; SPHERES; STRESSES; TUNGSTEN; VERY HIGH TEMPERATURE
- Descriptors DEC
- CRYSTAL DEFECTS; CRYSTAL STRUCTURE; CRYSTALS; DISPERSIONS; ELEMENTS; HEAT TREATMENTS; HOMOGENEOUS MIXTURES; LINE DEFECTS; MATERIALS; METALS; MICROSTRUCTURE; MIXTURES; SOLUTIONS; TRANSITION ELEMENTS