Synthesis and Characterizations of Fine Silica Powder from Rice Husk Ash

The silica content of rice husk ash obtained from the uncontrolled burning temperature of gasifier was 90.4%. The obtained rice husk ash was an amorphous form of silica with low crystallization by XRD. The sodium hydroxide solution, 1.5N, 2N, 2.5N and 3N, respectively was used to prepare sodium silicate solution by extraction method. The product silica was produced by acid precipitation method used 4.5N, 5.5N and 6.5N sulphuric acid solution. The highest yield percent of product silica extraced by 2.5N sodium hydroxide solution at 5N sulphuric acid solution was 88.84%. The crystallize size of product silica containing silicalite as a source of silica was 86nm at this condition. The fine silica powder was produced by acid refluxing mothod used 5.5N, 6N and 6.5N hydrochloric acid solution. 98% of pure fine silica powder can be produced from the product silica by refluxing method. The crystallize size of fine silica powder was 54nm. The distribution of the crystallize size of product silica powder could be found uniform in size and agglomeration. The Fourier Transform Infrared Spectra indicate the hydrogen bonded silinol groups and siloxane groups in product silica and fine silica powder.