Repeatability and Reproducibility of Fibre-Based Nanogenerator Synthesized by Electrospinning Machine

Zinc oxide fibres-based nanogenerators synthesized easily by electrospinning machine are promising to harvest electricity from mechanical energy. However, the repeatability and reproducibility were two major factors needed to be investigated to minimize product failure and to determine the feasibility of mass production of nanogenerators. The green fibres of zinc oxide were produced by electrospinning machine of zinc acetate and polyvinyl alcohol solution at a flow rate of 4 μL/min followed by sintering at temperature 550°C with heating rate 240°C/h. Each 10 nanogenerators was tested by three trained operators with three times of repetition at compressive load 0.5 kg. The nanogenerators revealed the maximum output voltage ranging from 203 to 217 mV. The value of repeatability and reproducibility of nanogenerators was approximately 24.29% showing that nanogenerators were still acceptable to be mass-produced. The relatively low reproducibility was mainly due to the operators, so that the checklist needed to be made easier and simpler for all the variables affecting to the quality of the fibres. Reducing the value of the repeatability and reproducibility is interesting to study further by creating a rotating collector so that the thickness and orientation of fibres can be arranged better