Effect of high temperature annealing on non-thermal equilibrium phases induced by energetic ion irradiation in FeRh and Ni3V intermetallic compounds

FeRh and Ni3V intermetallic compounds were irradiated with 16 MeV Au5+ ions and were subsequently annealed at elevated temperatures from 100 to 500°C. The non-thermal equilibrium A1 and L10 phases of FeRh, which were caused by the ion irradiation, disappeared by 300°C–100 min annealing. The non-thermal equilibrium A1 phase of Ni3V caused by the ion irradiation disappeared by 500°C–100 min annealing. The Vickers hardness for these two intermetallic compounds changes during the thermal annealing in a direction opposite to its change by the irradiation. The present experimental result shows that the combination of energetic ion irradiation and subsequent thermal annealing can be used as a useful tool for the modification of the mechanical properties of FeRh and Ni3V intermetallic compounds. (author)