Effect of pressure on the magnetic properties of TM3[Cr(CN)6]2·12H2O

We present the results of magnetization and AC susceptibility measurements performed on ferrimagnetic Mn32+[CrIII(CN)6]2·12H2O and ferromagnetic Ni32+[CrIII(CN)6]2·12H2O systems under pressures up to 0.9 GPa in a commercial SQUID magnetometer. The magnetization process is affected by pressure: magnetization saturates at higher magnetic field, saturated magnetization μs of Ni3[Cr(CN)6]2 is reduced and almost unaffected for Mn3[Cr(CN)6]2 at low temperatures. The Curie temperature TC of Mn3[Cr(CN)6]2 increases with the applied pressure, ΔTC/Δp = 25.5 K GPa-1, due to a strengthened super-exchange antiferromagnetic interaction JAF, but it is not affected significantly in the case of Ni3[Cr(CN)6]2 with a dominant ferromagnetic JF super-exchange interaction. The increase in the JAF interaction is attributed to the enhanced value of the single electron overlapping integral S and the energy gap Δ of the mixed molecular orbitals t2g (Mn2+) and t2g (CrIII) induced by pressure