Cathode polarization effect on the crack propagation rate during high-strength steels corrosion cracking in inhibited sodium chloride solutions
Description
An inhibitor concentration providing no defence against the general corrosion affects essentially the parameters of cathode polarization versus initial rate of cracks growth
Additional details
Additional titles
- Original title (Russian)
- О неоднозначном влиянии катодной поляризации на скорость роста трещины при коррозионном растрескивании высокопрочных сталей в ингибированных растворах хлористого натрия
Publishing Information
- Journal Title
- Fiz.-Khim. Mekh. Mater.
- Journal Volume
- 11
- Journal Issue
- 4
- Series
- Fiz.-Khim. Mekh. Mater.
- Journal Page Range
- 7-11
INIS
- Country of Publication
- USSR
- Country of Input or Organization
- USSR
- INIS RN
- 10423028
- Subject category
- S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY;
- Descriptors DEI
- AQUEOUS SOLUTIONS; CATHODES; CHEMICAL REACTION KINETICS; CHROMIUM STEELS; CORROSION INHIBITORS; CRACKS; DESTRUCTIVE TESTING; POLARIZATION; SODIUM CHLORIDES; STRESS CORROSION
- Descriptors DEC
- ALKALI METAL COMPOUNDS; ALLOYS; CARBON ADDITIONS; CHEMICAL REACTIONS; CHLORIDES; CHLORINE COMPOUNDS; CHROMIUM ALLOYS; CORROSION; DISPERSIONS; ELECTRODES; HALIDES; HALOGEN COMPOUNDS; HOMOGENEOUS MIXTURES; IRON ALLOYS; IRON BASE ALLOYS; KINETICS; MATERIALS TESTING; MIXTURES; REACTION KINETICS; SODIUM COMPOUNDS; SOLUTIONS; STEELS; TESTING; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- For English translation see the journal Sov. Mater. Sci.