The importance of the ultrasonic equivalent reflector size to the fracture mechanics - tested on heavy forgings for turbine-generators
Description
Specimens were machined from large forgings which had been rejected due to unacceptable ultrasonic indications. Simulating start/stop-cycles of turbine-generators the specimens were stressed in pulsating tension up to stress levels reaching the yield strength. After 25 000 cycles the specimens were broken open and the real sizes of the original defects and the crack propagation were measured. During several investigation steps ultrasonic examinations and partially magnetic particle testing were performed. The results showed that the ultrasonic testing indication amplitude expressed as an equivalent flat bottom hole diameter can be used for fracture mechanics calculations since the real crack propagation was always less than the crack propagation predicted on the basis of the ultrasonic testing results. (orig./HP)
Abstract (German)
Es wurden aus grossen Schmiedestuecken, die aufgrund unzulaessiger US-Befunde zu Ausschuss erklaert worden waren, Proben mit Fehlstellen gezielt entnommen. Diese wurden in Analogie zu den Start/Stop-Beanspruchungen von Turbomaschinen bis maximal zur Streckgrenze im Bereich bis zu 25 000 Lastwechseln zyklisch beansprucht. Danach wurden die Proben aufgebrochen und die Ursprungsfehlstellen und das Risswachstum exakt ausgemessen. Bei mehreren Untersuchungsschritten wurden jeweils Pruefungen mit US und z.T. mit Magnetpulver durchgefuehrt. Es zeigte sich, dass die US-Ersatzreflektorgroesse als Grundlage fuer bruchmechanische Berechnungen dienen kann, da das auf ihrer Basis berechnete und vorhergesagte Risswachstum in der Regel groesser als das tatsaechlich eingetretene Risswachstum der einzelnen Fehler war. (orig./HP)Additional details
Additional titles
- Original title (German)
- Die Bedeutung der Ultraschall-Ersatzreflektorgroesse fuer die Bruchmechanik, untersucht an schweren Schmiedestuecken fuer Turbomaschinen
Publishing Information
- Journal Title
- Materialpruefung
- Journal Volume
- 29
- Journal Issue
- 1/2
- Series
- Materialpruefung.
- Journal Page Range
- 13-16
- ISSN
- 0025-5300
- CODEN
- MTPRA
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 18065633
- Subject category
- S42: ENGINEERING; S22: GENERAL STUDIES OF NUCLEAR REACTORS; S36: MATERIALS SCIENCE;
- Descriptors DEI
- CRACK PROPAGATION; DEFECTS; DYNAMIC LOADS; FORGING; FRACTURE MECHANICS; TURBOGENERATORS; ULTRASONIC TESTING
- Descriptors DEC
- ACOUSTIC TESTING; ELECTRIC GENERATORS; ELECTRICAL EQUIPMENT; EQUIPMENT; FABRICATION; MATERIALS TESTING; MATERIALS WORKING; MECHANICS; NONDESTRUCTIVE TESTING; TESTING