Preparation of La0.8Sr0.2Cr0.97V0.03O3-δ films for solid oxide fuel cell application

La0.8Sr0.2Cr0.97V0.03O3-δ (LSC) is commonly studied as a ceramic interconnect material as well as a coating material for metallic interconnects for solid oxide fuel cell applications. However, it is difficult to sinter this type of material to high density. In order to overcome this problem and to study the material in form of a thin film we have used Pulsed Laser Deposition to obtain a dense, uniform film with the right stochiometry. Investigation of preparation-parameter dependence of the LSC films deposited on a stainless steel substrate during pulsed-laser deposition was carried out. The LSC films were deposited with KrF excimer laser (248 nm) on a stainless steel substrate at different oxygen pressure and substrate temperatures. The substrate temperature (873-1073 K) and the oxygen background pressure (5-20 Pa) were varied in order to obtain optimal growth conditions. The surface morphology and structural information of the films were obtained using scanning electron microscope (SEM) and X-ray diffraction, respectively. Under the optimal preparation-parameter conditions: substrate temperature of 1023 K and an oxygen pressure of 10 Pa the structure of the film agreed with the target structure and the SEM micrographs show that the surfaces are homogeneous, smooth, crack-free and dense