Peroxi-coagulation degradation of C.I. Basic Yellow 2 based on carbon-PTFE and carbon nanotube-PTFE electrodes as cathode

The electrochemical treatment of solutions containing C.I. Basic Yellow 2 (BY2) in aqueous solutions with carbon-PTFE (polytetrafluoroethylene) and carbon nanotube (CNT)-PTFE electrodes as cathode has been studied. The fabricated electrodes were characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The amount of electrogenerated H2O2 on the surface of these electrodes was investigated, too. The results showed that the amount of H2O2 obtained with the CNT-PTFE electrode was nearly three times higher than that of carbon-PTFE electrode. The decolorization efficiency of BY2 in peroxi-coagulation process reached 62% and 96% in the first 10 min by carbon-PTFE and CNT-PTFE electrodes at 100 mA, respectively. The effect of operational parameters such as applied current, initial pH and initial dye concentration was studied in an attempt to reach higher decolorization efficiency. The degradation and mineralization of BY2 using CNT-PTFE electrode were followed by total organic carbon (TOC) and GC-MS analysis. The results of TOC measurements indicated that peroxi-coagulation with carbon-PTFE allowed 81% mineralization after 6 h of electrolysis; whereas peroxi-coagulation with CNT-PTFE yields 92% mineralization under the same conditions. GC-MS analysis verified the identity of intermediates and a reaction pathway based on them was proposed.