Morphology, deformation, and defect structures of TiCr2 in Ti-Cr alloys

The morphologies and defect structures of TiCr2 in several Ti-Cr alloys have been examined by optical metallography, x-ray diffraction, and transmission electron microscopy (TEM), in order to explore the room-temperature deformability of the Laves phase TiCr2. The morphology of the Laves phase was found to be dependent upon alloy composition and annealing temperature. Samples deformed by compression have also been studied using TEM. Comparisons of microstructures before and after deformation suggest an increase in twin, stacking fault, and dislocation density within the Laves phase, indicating some but not extensive room-temperature deformability