High temperature oxidation of Zircaloy-2 and Zircaloy-4 in steam

At temperatures above the (α+β)/β transformation temperature for zirconium alloys, steam reacts with β-Zr to form a superficial layer of zirconium oxide (ZrO2) and an intermediate layer of oxygen-stabilized α-Zr. Reaction kinetics and the rate of growth of the combined (ZrO2+α-Zr) layer for Zircaloy-2 and Zircaloy-4 oxidation in steam were measured over the temperature range 1050-18500C. The reaction rates for both alloys were similar, obeyed parabolic kinetics and were not limited by gas phase diffusion. The parabolic rate constants were consistently less than those given by the Baker and Just correlation for zirconium oxidation in steam. A discontinuity was found in the temperature dependence of both the reaction rate and the rate of growth of the combined (ZrO2+α-Zr) layer. The discontinuity is attributed to a change in the oxide microstructure at the discontinuity temperature, an observation which is consistent with the zirconium-oxygen phase diagram. (Auth.)