Low alloy structural steels hardening in oxide melt when electric current flows through a specimen
Description
Low alloy structural steels surface layer hardening in a melt of oxides under electric current influence was considered. Microhardness increase results from the under-film layer enrichment with passivating elements-chromium, aluminium, nickel, molybdenum, silicon-containing in steels
Additional details
Additional titles
- Original title (Russian)
- Упрочнение низколегированных конструкционных сталей в оксидном расплаве при пропускании тока через образец
Publishing Information
- Journal Title
- Fizika i Khimiya Obrabotki Materialov
- Journal Issue
- no.1
- Journal Page Range
- p. 108-112.
- ISSN
- 0015-3214
- CODEN
- FKOMAT
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 26009767
- Subject category
- S36: MATERIALS SCIENCE; S36: MATERIALS SCIENCE;
- Descriptors DEI
- BORAX; MICROHARDNESS; STEEL-CRNI; SURFACE HARDENING; THERMODYNAMIC PROPERTIES
- Descriptors DEC
- ALKALI METAL COMPOUNDS; ALLOYS; BORATES; BORON COMPOUNDS; CARBON ADDITIONS; CHROMIUM ADDITIONS; COPPER ADDITIONS; HARDENING; HARDNESS; IRON ALLOYS; IRON BASE ALLOYS; LOW ALLOY STEELS; MECHANICAL PROPERTIES; NICKEL ADDITIONS; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; SODIUM COMPOUNDS; STEELS; SURFACE TREATMENTS