The effect of the Doping with Cobalt Transition Metal on the Dielectric and Structural Properties of Fe_0.5Co_xMg_0.95-xO Nanoparticles Synthesized by Sol-Gel Assisted Auto-Combustion

The compound Fe_0.5Co_xMg_0.95-xO where (x= 0.025, 0.05, 0.075, 0.1) was prepared via the sol-gel technique. The crystalline nature of magnesium oxide was studied by X-ray powder diffraction (XRD) analysis, and the size of the sample crystals, ranging between (16.91-19.62nm), increased, while the lattice constant within the band (0.5337-0.4738 nm) decreased with increasing the cobalt concentration. The morphology of the specimens was studied by scanning electron microscopy (SEM) which shows images forming spherical granules in addition to the presence of interconnected chips. The presence of the elements involved in the superposition was confirmed by energy-dispersive X-ray (EDX) analysis. The results showed that the dielectric constant decreases with increasing the cobalt concentration, while the dielectric loss factor and AC conductivity increase. (paper)