To the problem of structural materials serviceability in nitrogen-hydrogen-containing environments

The analysis of the factors which affect high-temperature serviceability of structural materials in nitrogen-hydrogen-containing environments, in particular in ammonia, has been carried out on the basis of the published and own experimental data. It is shown that the observed reduction of serviceability of structural materials, under the effect of high temperatures and nitrogen-hydrogen-containing environments, can occur as a result of corrosion failure connected with nitriding, and also hydrogen embrittlement appearing as a result of the penetration of hydrogen formed during adsorbed gaseous phase dissociation on the metal being deformed. The suggested scheme of high-temperature metal fracture under the effect of nitrogen-hydrogen-containing environments, that in contrast to the previous ones includes the factor of hydrogen ebrittlement, allows to give a real estimation of structional materials serviceability under product service conditions