Development of rubidium and niobium containing plastic foams. Final report

Rubidium fluoride and niobium metal-containing foam samples (rods and sheets) were prepared using two foam sytems: (1) hydrophilic polyurethanes prepared from W.R. Grace Co.'s Hypol prepolymers and (2) polyimides prepared from Monsanto Company's Skybond polyimide resin. The first system was used only for preparation of rubidium fluoride-containing foams while the second was used for both rubidium fluoride and niobium-containing foams. The niobium metal could readily be incorporated into the polyimide foam during molding, to produce foam sheets of the required dimensions and density. The rubidium fluoride-containing polyimide foams were preferably prepared by first rendering the molded polyimide foam hydrophilic with a postcuring treatment, then absorbing the rubidium fluoride from water solution. Similarly, rubidium fluoride was absorbed into the hydrophilic polyurethanes from water solution. Since the high reactive rubidium metal could not be employed, rubidium fluoride, which is very hygroscopic, was used instead, primarily because of its high rubidium content (approximately 82 weight percent). This was important in view of the low total densities and the high weight percentage rubidium required in the foam samples. In addition, at the later request of LLL, a block of rigid Hypol hydrophilic polyurethane foam (with a density of approximately 0.04 g/cm3 and cell sizes = or <0.2 mm) was prepared without any metal or metal compounds in it. Two shipments of foam samples, which met or closely approximated the project specifications, were submitted to LLL during the course of this project. Information on these samples is contained in Table 1. A complete description of their preparation is given in the Experimental Results and Discussion Section