Bonding of radioactive contamination. III. Auger electron spectroscopic investigation

The mechanisms by which radioactive contamination would be bonded to a DWPF canister surface are being investigated. Tests with low pressure water and air-injected water decontamination of radioactive specimens showed that bonding of contamination increases rapidly with postoxidation temperature. Even with the least severe temperature conditions expected on the waste glass canister, bonding is so great that decontamination cannot be affected by water-only techniques. A preoxidation film increased rather than decreased bonding. This memorandum describes detailed surface analyses of coupons simulating DWPF canister surfaces. Based on this examination we conclude: contamination will be dispersed throughout the oxide film on DWPF canisters. Contamination is concentrated at the surface, decreasing farther into the oxide film; some samples contain sludge contamination at the steel/oxide interface. This was not the case for semi-volatile (Cs2O) contamination; in samples with contamination at the steel/oxide interface, at least 80% of the contamination is usually in the oxide layer; no difference in contamination dispersion between preoxidized and non-preoxidized samples was found; and postoxidation atmosphere had no effect on the contamination dispersion within the oxide layer. 6 references, 9 figures