Interplay among solidification, microstructure, residual strain and hot tearing in B206 aluminum alloy

Hot tearing is a complex phenomenon attributed to alloy solidification, microstructure and stress/strain development within a casting. In this research, the conditions associated with the formation of hot tears in B206 aluminum alloy were investigated. Neutron diffraction strain mapping was carried out on three B206 castings with varying levels of titanium (i.e. unrefined, 0.02 and 0.05 wt%). Titanium additions effectively reduced grain size and transformed grain morphology from coarse dendrites to fine globular grains. Further, thermal analysis suggested that grain refinement delayed the onset of dendrite coherency in B206 and therefore enhanced the duration of bulk liquid metal feeding for the refined casting conditions. As a result, the interactive effects of such factors resulted in a more uniform distribution of strain, and subsequent higher resistance to hot tearing for the grain refined castings