Principles of alloying of Ni superalloys resistant to high-temperature corrosion
Creators
- 1. Zaporozhskij Natsional'nyj Tekhnicheskij Univ., Zaporozh'e (Ukraine)
Description
The effect of alloying elements (Cr, Ti, Al, Co, W, Nb) on resistance against high-temperature corrosion of the nickel alloys, applied in the gas turbine building, is studied. The diagram of the alloys heat resistance level dependence on the alloying elements concentration is plotted, wherein three areas are separated: 1) the area of improved heat resistance due to the solid solution and dispersion strengthening; 2) the area of decreasing heat resistance due to formation of the carbide net by the grain boundaries; 3) the area of catastrophic decrease in the heat resistance by separation of the embrittlement topologically close-packed phases. The class of the high-temperature corrosion-resistant nickel alloys with different chromium content (13-30%), the Ti/Al > 1 concentration ratio and balanced content of high-melting and rare earth elements is created
Abstract (Russian)
Исследовано влияние легирующих элементов (Cr, Ti, Al, Co, W, Nb) на стойкость высокотемпературной коррозии никелевых сплавов, применяющихся в газотурбостроении. На основании экспериментальных данных построена диаграмма зависимости уровня жаропрочности сплавов от концентрации легирующих элеметов, в которой выделены три области: 1) область улучшения жаропрочности в результате твердорастворного и дисперсионного упрочнения; 2) область снижения жаропрочности из-за образования карбидной сетки по границам зерен; 3) область катастрофического снижения жаропрочности при выделении охрупчивающих топологически плотноупакованных фаз. Создан класс жаропрочных коррозионностойких никелевых сплавов с различным содержанием хрома (13-30%), отношением концентраций Ti/Al > 1 и сбалансированным содержанием тугоплавких и редкоземельных элементовAdditional details
Additional titles
- Original title (Russian)
- Принципы легирования жаропрочных никелевых сплавов, стойких к высокотемпературной коррозии
Publishing Information
- Journal Title
- Metallovedenie i Termicheskaya Obrabotka Metallov
- Journal Issue
- no.10
- Journal Page Range
- p. 5-9
- ISSN
- 0026-0819
- CODEN
- MTOMAX
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 33047774
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ALUMINIUM ALLOYS; CHEMICAL COMPOSITION; CHROMIUM ALLOYS; COBALT ALLOYS; CONCENTRATION RATIO; CORROSION RESISTANCE; CORROSION RESISTANT ALLOYS; HEAT RESISTING ALLOYS; MOLYBDENUM ALLOYS; NICKEL BASE ALLOYS; PHASE STUDIES; TEMPERATURE RANGE 1000-4000 K; TITANIUM ALLOYS; TUNGSTEN ALLOYS
- Descriptors DEC
- ALLOYS; HEAT RESISTANT MATERIALS; MATERIALS; NICKEL ALLOYS; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 1 fig.