Electric and magnetic properties of oxidic titanium bronzes of rare earths Lnsub(2/3+x)TiOsub(3+-y) with perovskite structure

A study was made on electric and magnetic properties of oxidic titanium bronzes of rare earths and their dependence on rare earth nature and the degree of rare earth sublattice filling was followed. Data on Lnsub(2/3)TiOsub(3-y) (Ln-Ce, Nd) anion-deficient perovskites are given as well. Investigated Cesub(2/3)TiOsub(2.985) and Ndsub(2/3)TiOsub(2.875) phases as well as defectless with respect to oxygen Lnsub(2/3)TiOsub(3) phases have rhombic structure of perovskite type with ordered position of Ln3+ cations and vacancies. Specific electric resistance and thermoelectromotive force factor were determined in vacuum at 290-1173 K for samples in the form of parallelepiped of 3x5x25 mm3 size. Magnetic susceptibility chi was determined at 77-300 K by Faraday method using a device based on magnetic balancewith electromagnetic compensation. Relative error during chi measuring didn't exceed +-2%. Collectivized behaviour of d-electrons of Ti3+ cations in oxidic titanium bronzes of rare earths: Lnsub(2/3+x)TiOsub(3+-y) (Ln-La, Ce, Nd; 0 < x < 1/3), conditioned by formation of narrow, partly filled π*-zone, was established on the basis of measuring specific electric resistance and magnetic susceptibility