Guidelines for prediction of irradiation embrittlement of operating WWER-440 reactor pressure vessels

This TECDOC has been developed under an International Atomic Energy Agency Coordinated Research Project (CRP) entitled Evaluation of Radiation Damage of WWER Reactor Pressure Vessels (RPV) using Database on RPV Materials to develop the guidelines for prediction of radiation damage to WWER-440 PRVs. The WWER-440 RPV was designed by OKB Gidropress, Russian Federation, the general designer. Prediction of irradiation embrittlement of RPV materials is usually done in accordance with relevant codes and standards that are based on the large amounts of information from surveillance and research programmes. The existing Russian code (standard for strength calculations of components and piping in NPPs - PNAE G 7-002-86) for the WWER RPV irradiation embrittlement assessment was approved more than twenty years ago and based mostly on the experimental data obtained in research reactors with accelerated irradiation. Nevertheless, it is still in use and generally consistent with new data. The present publication presents the analyses using all available data required for more precise prediction of radiation embrittlement of WWER-440 RPV materials. Based on the fact that it contains a large amount of data from surveillance programmes as well as research programmes, the IAEA International Database on RPV Materials (IDRPVM) is used for the detailed analysis of irradiation embrittlement of WWER RPV materials. Using IDRPVM, the guideline is developed for assessment of irradiation embrittlement of RPV ferritic materials as a result of degradation during operation. Two approaches, i.e. transition temperatures based on Charpy impact notch toughness, as well as based on static fracture toughness tests, are used in RPV integrity evaluation. The objectives of the TECDOC are the analysis of irradiation embrittlement data for WWER- 440 RPV materials using IDRPVM database, evaluation of predictive formulae depending on chemical composition of the material, neutron fluence, flux, and development of guidelines for prediction of radiation embrittlement of WWER-440 of operating reactor pressure vessels including methodology for evaluation of surveillance data of a specific operating unit