Surface characteristics of aluminum 6061 T6 subjected to Nd:YAG pulsed laser irradiation

The objective of this study was to investigate the surface characteristics of an aluminum 6061 T6 alloy subjected to Nd:YAG pulsedlaser irradiation. The test specimens were prepared by a mechanical polishing process using diamond paste and emery polishing paper to obtain different levels of initial surface roughness. After ten pulsed laser shots, the surface morphology was observed via optical microscopy (OM) and scanning electron microscopy (SEM). Nano indentation hardness testing was also conducted on the irradiated surface. The diameter of the melted zone increased with surface roughness because of the multiple reflection and absorption of the laser beam. The relative absorbance was measured as a function of the diameter of the melted zone with varied surface roughness