Examination of temperature-induced shape memory of uranium--5.3-to 6.9 weight percent niobium alloys

The uranium-niobium alloy system was examined in the range of 5.3-to-6.9 weight percent niobium with respect to shape memory, mechanical properties, metallography, Coefficients of linear thermal expansion, and differential thermal analysis. Shape memory increased with increasing niobium levels in the study range. There were no useful correlations found between shape memory and the other tests. Coefficients of linear thermal expansion tests of as-quenched 5.8 and 6.2 weight percent niobium specimens, but not 5.3 and 6.9 weight percent niobium specimens, had a contraction component on heating, but the phenomenon was not a contributor to shape memory