Thermal analysis, spectra and laser properties of a new Yb3+-doped multicomponential tellurite-based glass

A series of new glasses of 70TeO2-(20-x) ZnO-xGeO2-5La2O3-2.5K2O-2.5Na2O (mol%) doped with Yb3+ is presented. Thermal analysis, spectra and laser properties of Yb3+ ions have been measured. It is found that 70TeO2-20GeO2-5La2O3-2.5K2O-2.5Na2O composition glass had better thermal stability than 75TeO2-20ZnO-5Na2O glass, higher stimulated emission cross-section of 1.23 pm2 for the 2F5/2→2F7/2 transition close to PN glass, lower minimum pump intensity of 0.98 KW/cm2, long fluorescence lifetime of 0.92 ms and the broad fluorescence effective line width of 77 nm. Evaluated from the good potential laser parameters, this system glass is a promising host of miniature solid lasers such as short pulse generation in diode pumped lasers, short pulse generation tunable lasers, high-peak power and high-average power lasers, etc