Neutron induced damage in reactor pressure vessel steel: An X-ray absorption fine structure study

The radiation damage produced in reactor pressure vessel (RPV) steels during neutron irradiation is a long-standing problem of considerable practical interest. In this study, an extended X-ray absorption fine structure (EXAFS) spectroscopy has been applied at Cu, Ni and Mn K-edges to systematically investigate neutron induced radiation damage to the metal-site bcc structure of RPV steels, irradiated with neutrons in the fluence range from 0.85 to 5.0 x 1019 cm-2. An overall similarity of Cu, Ni and Mn atomic environment in the iron matrix is observed. The radial distribution functions (RDFs), derived from EXAFS data have been found to evolve continuously as a function of neutron fluence describing the atomic-scale structural modifications in RPVs by neutron irradiations. From the pristine data, long range order beyond the first- and second-shell is apparent in the RDF spectra. In the irradiated specimens, all near-neighbour peaks are greatly reduced in magnitude, typical of damaged material. Prolonged annealing leads annihilation of point defects to give rise to an increase in the coordination numbers of near-neighbour atomic shells approaching values close to that of non-irradiated material, but does not suppress the formation of nano-sized Cu and/or Ni-rich-precipitates. Total amount of radiation damage under a given irradiation condition has been determined. The average structural parameters estimated from the EXAFS data are presented and discussed