Single-pass continuous-flow leach test of PNL 76-68 glass: some selected Bead Leach I results

A single-pass continuous-flow leach test of PNL 76-68 glass beads (7 mm dia) was concluded after 420 days of uninterrupted operation. Variables included in the experimental matrix were flow-rate, leachant composition, and temperature. Analysis was conducted on all leachate samples for 237Np and 239Pu as well as a number of nonradioactive elements. Results indicated that flow-rate and leachant systematically affected the leach rate, but only slightly. Temperature effects were significant. Plutonium leach rate was lower at higher temperature suggesting that Pu sorption onto the beads was enhanced at the higher temperature. The range of leach rates for all analyzed elements (except Pu), at both temperatures, at all three flow rates, and with all three leachant compositions varied over only three orders of magnitude. The range of variables used in this experiment covered those expected in many proposed repository environments. The preliminary interpretation of the results aPPh3 also reacted with Mn2(CO)10 and Cp2Mo2(CO)6 to give a variety of products at room temperature. A radical mechanism was suggested