Uranium determination in U-Al alloy with statistical tools support

ICP-OES was used to quantify total uranium in natural UAlx powder alloy. A simple solubilisation procedure using diluted HNO3/HCl was successfully applied. Only 100 mg of sample were used which is an advantage over the volumetric methodologies. Only two dilutions were needed to reach measurable concentration. No other treatment was applied to the solutions. Calibration curves of three uranium lines (367.007, 385.958 and 409.014 nm) were evaluated using ANOVA. Comparing the indicators, the 367.007 nm line was the poorer one but exhibiting a R2 = 0.998 and 0.9996 and 0.999 for the other two lines. No significant difference was found between these two lines. If needed, the 385.958 nm line could be used to quantify uranium in very low concentrations but with few advantages over the 409.014 nm line, if so. The average uranium concentration found was 0.80±0.01 μg.g-1, as expected for a predominant UAl2 phase alloy. Higher uranium concentrations are also expected to be successfully quantified using these lines. In order to verify possibly inhomogeneity due to the high uranium concentration, one-way ANOVA was applied to 3 replicates. Homogeneity was confirmed measuring in both 385.958 and 409.014 nm lines. The uncertainty of solution homogeneity was estimated also in these two emission lines giving 0.006 and 0.005 μg.g-1, respectively. These two values are in compliance with the standard deviation of the average. (author)