Materials and coating technology for pyrochemical reprocessing applications

Metallic fuelled fast breeder reactors with co-located pyrochemical reprocessing plants have been proposed as the best option in order to increase the breeding gain, reduce the doubling time of the fuel and reprocess short cooled and high burnup fuel. To establish the pyrochemical reprocessing plants with various unit operations, it is necessary to identify, develop and qualify reliable corrosion resistant materials and coatings for service in molten LiCI-KCI salt and molten uranium environment operating at 773 to 1573 K. Towards materials and coating technology development and testing for molten salt environment a high temperature corrosion testing laboratory was established and studies were initiated. Molten salt test assembly for testing materials and coatings in molten LiCI-KCI salt under controlled ultra high pure (UHP) argon environment at high temperatures has been designed, fabricated, commissioned and tests were carried out on various candidate materials and coatings. Electro-formed (EF) Ni, Ni with Ni-W coating, coatings of ZrN, TiN, HfN and Ti-Si-N on high density (HD) graphite, candidate materials like 2.25Cr-1Mo steel, 9Cr-1Mo steel, 316L stainless steel, Ni base alloys (INCONEL 600, 625 and 690), HD graphite, pyrolytic graphite (PyG), and yttria stabilized zirconia (YSZ) and alumina-40wt% titania thermal barrier coatings were tested for their suitability for molten salt applications. Corrosion studies indicated that YSZ and PyG showed superior corrosion resistance in molten LiCI-KCI salt at 873 K up to 2000 h exposure. Surface modification techniques like annealing, laser remelting and laser shock processing were pursued to consolidate the coatings and improve their high temperature performance. Coating integrity using dielectric electrochemical system and thermal cycling furnace established that, compared to plain 9Cr-1Mo steel YSZ coated 9Cr-1Mo steel performed better from 473 K to 1223 K. The presentation highlights the results of the investigations carried out towards development of materials and coatings technology for pyrochemical reprocessing applications. (author)