Electromechanical performance of an ionic polymer–metal composite actuator with hierarchical surface texture

Two stainless steel templates were fabricated using electric-spark machining, and a hierarchical surface texture of ionic polymer was produced using both polishing and replication methods, which produced microscale and nanoscale groove-shaped microstructures at the surface of the polymer. The surface morphology of the Nafion membrane and metal electrode were observed using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). SEM and EDS line-scan analysis indicated that the interfacial surface area was considerably increased and an excellent metal electrode was obtained with the production of a hierarchical surface texture. The displacement, blocking force, and electric current were measured using home-built apparatus. The results revealed that the combined polishing and replication method significantly improved the electromechanical performance of the ionic polymer–metal composite (IPMC). Compared with sandblasted Nafion-based IPMC, the blocking force, displacement, and electric current of the replicated Nafion-based IPMC were 4.39, 2.35, and 1.87 times higher, respectively. The IPMC fabricated in this work exhibited a competitive blocking force compared with recently reported actuators. (paper)