Analysis of steam generator tube sections removed from Gentilly-2 nuclear generating station

In order to meet the requirements of CSA Standards CAN/CSA N285.4-94, which states, 'A section of one tube in a deposit region shall be removed from one steam generator for metallurgical examination', Gentilly-2 has been removing steam generator tube sections on a regular basis for analysis at Chalk River Laboratories. In 2009 April, sections from the hot leg and the cold leg of a steam generator tube were removed for detailed metallographic examination and characterization. The hot leg tube section covered the area from within the tube sheet up to below the second support plate, and the cold leg tube section covered the area from within the tube sheet to below the third preheater support plate. After a general visual and photographic examination, the area above the tube sheet on the hot leg side where the sludge pile is highest was examined in detail. Visual and macro-photography of the two tube sections within the tube sheet were also examined. Additional metallographic and surface examinations of both tube inner diameter and tube outer diameter, and surface roughness measurements of tube inner diameter were also completed. The surface activities (μCi/cm²) of cold leg and hot leg specimens were measured before and after electrolytic descaling, and major and minor radionuclides were identified; a comparison of the surface activities for hot leg with the values for the cold leg were made. The results from the initial γ-spectroscopy measurements, and the measurements after the descaling of the specimens were used to estimate decontamination factors for each specimen and for each radionuclide. The tube specimens had thin outer diameter oxides; all four steam generators were chemically cleaned in 2005. All specimens had inner diameter deposits; the inner diameter deposits on the cold leg were heavier than those on the hot leg as expected. Primary side oxide loadings of specimens were used to estimate the total oxide inventory in 2009. The oxide deposition rate in the steam generators from 2001 to 2009 were estimated and compared to the estimated values from 1983 (station commissioning) to 2001. This paper presents a summary of steam generator tube characterization results and describes how the data on the oxide deposition rate were correlated to the changes in station operating practices. These data demonstrate the benefits that resulted from recent changes to station chemistry and operational practices. (author)